Formation of interfacial voids in cast and micro-grained γ′-Ni3Al during high temperature oxidation

Specimens of cast and micro-grained γ′-Ni3Al, which were produced with vacuum casting and unbalanced magnetron sputter deposition, respectively, were isothermally oxidised in air at 1473 K for different periods of time. The formation of interfacial voids at the alloy/oxide interface was observed with SEM, which indicated that there were more interfacial voids formed in the cast Ni3Al than in the micro-grained alloy under the same oxidation conditions. A phenomenological equation describing the fraction of the void projected areas was established, in which the impingement and coalescence between voids during their growth was taken into consideration. It was elucidated that low vacancy density in the micro-grained Ni3Al due to the high creep, re-crystallisation and the enhanced Al diffusion reduced the void percentage. Also, it was confirmed that aluminium evaporation, perhaps supplemented by surface diffusion, supplied most Al to the oxide scales formed above the interfacial voids.