Phase equilibria in the system Al–Co–Si

The Al–Co–Si system was studied for three isothermal sections at 600 °C (equilibria with Si), 800 °C (alloys up to 50 at.% Co) and 900 °C (alloys with more than 50 at.% Co). A total number of seven ternary compounds were characterized in the ternary system and the homogeneity ranges of the various ternary solid solutions of binary Co–Al and Co–Si compounds were studied. X-ray powder diffraction and optical microscopy was used for initial sample characterization and electron probe microanalysis of the annealed samples was used to determine the phase compositions within the ternary system. Lattice parameters have been determined for all ternary compounds and the change of lattice parameters with the composition is given for the solid solution phases.