Dependence of the brittle-to-ductile transition temperature (BDTT) on the Al content of Fe–Al alloys

The brittle-to-ductile transition temperature (BDTT) of binary Fe–Al alloys with between 9.6 and 45 at.% Al was investigated in the as-cast state by four-point bending tests. An increase of the BDTT was observed with increasing aluminium content between 9.6 and 19.8 at.%. Up to 41.3 at.%, the BDTT did not change significantly. A sharp increase of the BDTT occurred between 41.3 and 45 at.% Al. Transgranular cleavage was observed at a composition of 25 at.% Al, mixed-mode fracture between 39.6 and 41.3 at.% Al and intergranular fracture at 45 at.% Al. The results indicate that the increase in BDTT is correlated with the transition from mixed-mode to intergranular fracture.