The effect of Ti-addition on plastic deformation and fracture behavior of directionally solidified NiAl/Cr(Mo) eutectic alloys

To improve the high-temperature strength of NiAl/Cr(Mo) eutectic alloys, the effect of Ti-addition on microstructure and mechanical properties was examined. Three directionally solidified (DS) alloys with the composition of Ni–(33 − x)Al–31Cr–3Mo–xTi (x = 0, 3 and 5 at.%, respectively), denoted 0Ti-, 3Ti- and 5Ti-alloys hereafter, were prepared. Temperature dependence of the yield stress and the room temperature fracture toughness of these DS alloys was examined. The aligned lamellae with B2-NiAl and A2-Cr(Mo) were formed in 0Ti-alloy, but the formation of lamellar structure was hindered by the Ti-addition. Cellular microstructures containing short plate shapes of Cr(Mo) phases were obtained in 3Ti- and 5Ti-alloys. In 5Ti-alloy, the precipitation of the L21-Ni2AlTi was confirmed in NiAl matrix phase after the DS treatment. The Ti-addition induced a significant increase in high-temperature strength accompanied by a large deterioration of room temperature fracture toughness. The fracture toughness of 5Ti-alloy showed the low value of about 4 MPa m1/2 because of the disturbance of microstructure.