Grain refinement of a Fe3Al-based alloy using κ-Fe3AlC precipitate particles stimulating nucleation of recrystallization

Effects of particle distribution level on recrystallization were investigated in a Fe3Al-based alloy containing coarse κ-Fe3AlC precipitate particles. Volume fraction of 10–12% of rod-like κ particles with different size and interparticle spacing was introduced within the Fe3Al matrix by changing the cooling rate from 1200 °C, which is above the precipitation temperature of the κ phase. These samples were warm rolled at 700 °C to a total reduction of 75%. Annealing of the warm rolled samples produced complete recrystallized structures. The average recrystallized grain size against interparticle spacing showed a valley-shaped curve with a minimum size of ∼20 μm. Orientation analyses of the warm rolled samples with high resolution EBSD method revealed that the valley shape of the curve may be explained by the particle stimulated nucleation density of recrystallization around κ particles, dependent on the particle distribution.