ETBE synthesis over silicotungstic acid and tungstophosphoric acid catalysts calcined at different temperatures

Vapor phase ethyl tertiary butyl ether synthesis was investigated using heat treated heteropoly acid catalysts, namely silicotungtsic acid (STA) and tungstophosphoric acid-Keggin (TPA-K) and these results were compared with the results obtained with untreated catalysts. ETBE synthesis experiments showed that heat treatment of TPA-K at temperatures over 473 K had caused significant decrease of its catalytic activity. Activity of STA was more stable and deactivation of this catalyst was observed by heat treatment at 673 K and above. Heat treatment at high temperatures caused loss of constitutional water of STA and TPA-K, causing loss of protons, consequently the loss of acidity of the catalysts, resulting deactivation. FT-IR, TGA–DTA and DRIFTS analyses on pyridine-adsorbed catalysts supported the conclusions related to structural changes of STA and TPA-K with heat treatment. Highest ETBE yields were obtained at around 368 K, while at temperatures over 423 K formation of DEE and ethylene were observed due to dehydration of ethanol.