Compression load failure of aluminum plates due to fire

An experimental study was performed to quantify the response and failure of 5083-H116 and 6082-T6 aluminum plates under compression load while being subjected to a constant heat flux representing a fire exposure. Using an intermediate scale loading frame with integrated heating, the study evaluated the effects of geometry, aluminum type, fire exposure, load, and fire protection. Intermediate scale aluminum panels which were more than 0.7 m high and 0.2 m wide were used to gain insights into the structural behavior of large structural sections exposed to fire. Failure temperatures were measured to range from 100 to 480 °C and were dependent on applied stress and aluminum type. This indicates that the use of a single temperature criterion in fire resistance without load as typically done is not sufficient for evaluating structural response during fire. An empirical failure model was developed to account for fire exposure conditions, aluminum type, and geometry.