Investigations of hydrogen storage properties in certain Zr-based AB2 alloys

The hydrogen storage properties of ZrMnFe0.45Co0.45V0.1 and ZrMn0.9V0.1Fe0.5Co0.5, which are of C14 hexagonal structure, are studied in the ranges of 0.3⩽P (bar)⩽30 and 30⩽T (°C)⩽100. The partial substitution of V at the Mn site or at the Fe/Co site in ZrMnFe0.5Co0.5 leads to the expansion of the lattice, the percentage of volume expansion being larger for ZrMnFe0.45Co0.45V0.1 than for ZrMn0.9V0.1Fe0.5Co0.5. The pressure–composition (P–C) isotherms of ZrMnFe0.45Co0.45V0.1 and ZrMn0.9V0.1Fe0.5Co0.5 show the existence of α, (α+β) and β regions. The hydrogen desorption isotherms of the alloys show that the hysteresis is small. ateau pressures of ZrMnFe0.45Co0.45V0.1–H in the temperature ranges investigated, are lower than those in ZrMn0.9V0.1Fe0.5Co0.5–H, due to the larger size of the tetrahedral interstitial sites in the former alloy. The dependence of the relative partial molar enthalpy of dissolved hydrogen (ΔHH) and the partial molar entropy of dissolved hydrogen (ΔSH) in ZrMnFe0.45Co0.45V0.1–H and ZrMn0.9V0.1Fe0.5Co0.5–H on the hydrogen concentration show the presence of α, (α+β) and β phases. The chemical potential of dissolved hydrogen (ΔμH) in ZrMnFe0.45Co0.45V0.1–H is larger than that in ZrMn0.9V0.1Fe0.5Co0.5–H due to the larger size of the tetrahedral interstitial sites in the former alloy.