Crystallographic and electrochemical characteristics of melt-spun Ti–Zr–Ni–Y alloys

Ti45Zr30Ni25Yx (x = 1, 3, 5 and 7) alloys were prepared by melt-spinning at wheel velocity of 20 m s−1. The effect of additive Y on phase structure and electrochemical performance of melt-spun alloys was investigated. Ti45Zr30Ni25Yx melt-spun alloys were composed of I-phase and amorphous phase. The amorphous phase increased with increasing x value, indicating amorphous forming ability improved with increasing Y content. The maximum discharge capacity and high-rate dischargeability decreased with increasing x value, which may be ascribed to the decrease of nickel content. Cycling stability first increased with increasing x from 1 to 3, and then decreased when x increased to 7, which was resulted from the combined effect of the decrease of nickel content and the increase of amorphous phase.