Hydrogen storage in Co-and Zn-based metal-organic frameworks at ambient temperature

Hydrogen adsorption properties of some Co-and Zn-based Metal-Organic Framework (MOF) materials were studied at near ambient temperatures. Maximal hydrogen storage capacity of 0.75 wt% was found for a Zn-based material at 175 Bar hydrogen pressure and T = −4 °C. Hydrogen adsorption correlated linearly with BET surface area and strongly depends on temperature. Relatively low structural stability of some MOFʹs results in framework collapse during degassing and hydrogen adsorption measurements.