Magnetic pole pinning at rectangular defects on MnAs/GaAs(0 0 1)

Strong magnetic poles at characteristic rectangular defects have been observed using a magnetic force microscope on a MnAs(1̄ 1 0 0) thin film with the thickness of 30 nm. The MnAs thin film was epitaxially grown on a GaAs(0 0 1) substrate. The magnetic poles were in one-arranging direction, being independent of the magnetization direction of the film. The poles were pinned at the edges of the rectangular defects until just below the Curie temperature, and formed a stable magnetic-field loop on the MnAs surface. The stability of the magnetic pole pinning shows the distinctive feature of the magnetic domain structure on the surface with a strong anisotropy, which was built in the heterostructure of MnAs and GaAs.