Preparation and characterization of sol–gel derived mesoporous titania spheroids

The formation of mesoporous spherical titania particles via hydrolysis of pure titanium tetra-isopropoxide in n-heptane solution upon the application of a slow stirring rate is described. Calcination of the dry hydrolysis product produced pure anatase at 400–600°C, and rutile at 800°C. Nitrogen adsorption results indicate high surface area (SBET 132 m2/g) and uniform mesopores peaking at 10 nm for the material calcined at 400°C. Upon calcination at 600°C, the pore size remained at 10 nm, whereas the SBET value was decreased. The material calcined at 400°C was found by scanning electron microcopy to be shaped into spherical particles about 2 μm in diameter. Sizes of the spherical particles were unchanged at 400°C and up to 800°C. This was ascribed to the spherical morphology of the particles which prevented primary particles from growing beyond the boundary of the host aggregate even when the rutile phase transition occurred at 800°C.