Valence variations of Sm on polycrystalline Ag

Thin deposited films of Sm on a polycrystalline Ag are investigated by X-ray photoelectron spectroscopy (XPS), ultraviolet photoelectron spectroscopy (UPS) and photoemission electron microscopy (PEEM). The Sm valence is mainly divalent for low Sm coverage, while the trivalent contribution to the XPS intensity increases considerably for higher coverage. For an Sm overlayer thicker than 4 إ, the average valence is estimated to be 2.65. The mixed valence in this system is concluded to be heterogeneous (all Sm atoms have integer and site-dependent valence). Alloy formation between Sm and Ag is observed upon annealing to temperatures between 400 and 550 °C. For these temperatures the change in average Sm valence is dependent on the initial Sm coverage deposited onto the Ag-foil. Systems with low initial coverage exhibit an increase in the average valence, while a decrease is observed for systems with coverage above 6 إ. For intermediate coverages around 3 إ an initial decrease in average valence is followed by a rapid increase for temperatures above 400 °C due to morphological changes in the surface layer.