Hygrothermal ageing of adhesive joints with nanoreinforced adhesives and different surface treatments of carbon fibre/epoxy substrates

The effect of water absorption on the strength of single lap adhesive joints subjected to accelerated hygrothermal ageing (55 °C, 95% relative humidity, 800 h) was analysed. Two different variables were studied: the surface treatment of the carbon fibre/epoxy laminates (peel ply, grit blasting and atmospheric pressure plasma) and the addition of carbon nanofillers (0.5 wt% nanofibres and 0.25 wt% nanotubes) to the epoxy adhesive. The joint strength and the failure mode of the joints were investigated. Furthermore, the amount of water absorbed by the adhesive was determined. ve joints with peel ply-treated laminates exhibit an increase in their strength, which is attributed to a relaxation of stresses in the adhesive/laminate interface; with grit blasting, this property remains almost constant. Plasma treatment provides the worst ageing behaviour because this treatment results in a surface with a higher surface free energy, which is more susceptible to environmental attack. The nanoreinforcement of the adhesive has a beneficial effect: it decreases the amount of absorbed water.