Growth of Pt thin films on WSe2

The morphology and structure of Pt deposited on a WSe2(0 0 0 1) van der Waals surface have been investigated by reflection high energy electron diffraction and scanning tunneling microscopy. At room temperature, the initial growth is characterized by the formation of three-dimensional fcc Pt islands with (1 1 1) orientation. In contrast, at higher temperatures of about 450 °C the formation of a novel chemically ordered Pt–Se alloy is observed. Based on the diffraction patterns, a tetragonal DO22-type structure of a Pt3Se compound is suggested. With increasing Pt thickness, this chemically ordered alloy disappears and an additional superstructure occurs, which is accompanied by the coalescence of the islands. The observed superstructure is attributed to a strong Se diffusion towards the growth surface, forming most likely a PtSe2 alloy with the CdI2-type layered structure on the top surface. Due to the lateral lattice mismatch between the Pt(1 1 1) layers and the PtSe2(1 1 1) top layer, a Moiré pattern with a period of 1.1 nm is created, which might be used as a long-range atomic pattern for further nanostructure growth.