Oxygen permeation of SrFe0.67Co0.33O3−d
Author/Authors :
Aasland، نويسنده , , S and Tangen، نويسنده , , I.L and Wiik، نويسنده , , K and طdegهrd، نويسنده , , R، نويسنده ,
Issue Information :
دوهفته نامه با شماره پیاپی سال 2000
Pages :
5
From page :
713
To page :
717
Abstract :
Oxygen permeation fluxes through dense SrFe0.67Co0.33O3−d membranes have been measured as a function of temperature, oxygen partial pressure gradient across the membrane, and membrane thickness. A maximum oxygen flux of 2.74 sccm/min cm2 (1.87×10−6 mol/s cm2) was measured at 1000°C with air on the primary side, and He on the secondary side of the SrFe0.67Co0.33O3−d membrane. Activation energies from 88 to 108 kJ/mol were found in the temperature range between 900 and 1000°C. At 1000°C with He on the secondary side of the membrane, a critical thickness of roughly 1.5 mm was found for SrFe0.67Co0.33O3−d where the rate limiting step for oxygen permeation changed from surface exchange kinetics to bulk diffusion. The critical thickness appears to be dependent on the temperature and the pO2 gradient across the membrane.
Keywords :
Activation energy , Oxygen permeation , SrFe0.67Co0.33O3?d , Critical thickness , Rate limiting step
Journal title :
Solid State Ionics
Serial Year :
2000
Journal title :
Solid State Ionics
Record number :
1707618
Link To Document :
بازگشت