Properties of ultrasound-assisted blends of poly(ethylene terephthalate) with polycarbonate

This study investigated the effect of ultrasound irradiation on blends of polyethylene terephtalate (PET) and polycarbonate (PC). The blends of PET/PC were prepared by a twin-screw extruder with an attached ultrasonic device. Thermal, rheological, and mechanical properties and morphology of the blends with and without sonication have been analyzed. The two distinct Tgs of the blends measured by DSC showed immiscibility over all compositions. The theoretical PET content that is miscible in PC-rich phase calculated using the Fox equation showed that ultrasonic waves made the blends more miscible. From mechanical test results, when sonication was not applied, the 20/80 blend was the most miscible composition. At that composition, the impact strength of sonicated blend was surprisingly high. It was believed to be due to the enhancement of compatibility by a reaction such as transesterification. The results from the morphology of the 20/80 sonicated blend were in agreement with DSC and impact test results.