Stability and oxygen transport property of La0.8Sr0.2Cr0.5Fe0.5O3 -δ

The stability of La0.8Sr0.2Cr0.5Fe0.5O3 -δ (LSCrF) in reducing atmosphere was investigated by examining the extent of its reaction with hydrogen at elevated temperature. LSCrF powder exposed to diluted hydrogen was found to loss a weight of only ~ 0.5%, corresponding to the formation of oxygen vacancies in the lattice. LSCrF powder exposed to flowing concentrated hydrogen for 30 h was found to decompose partially. The decomposition oxygen partial pressure of LSCrF at 950 °C was estimated to be 6.3 × 10− 28 atm from thermodynamic calculations. The stability of LSCrF under an oxygen chemical potential gradient was also examined by exposing a disk-shaped dense sample to air at one side and to reducing atmosphere (CO) at the other side at elevated temperatures. A thin, porous layer was found to form on the CO side surface. An oxygen permeation flux of 2.5 × 10− 7 mol cm− 2 s− 1 was observed at 950 °C under given air/CO gradient. The occurrence of oxygen permeation revealed the presence of mixed oxygen ionic and electronic conductivity. The oxygen ionic conductivity was estimated to be ~ 0.01 S/cm at 950 °C.