Premade versus in situ formed compatibilizer at the PS/PMMA interface: contribution of the Raman confocal microscopy to the fracture analysis

The interface of a two-layer assembly of polystyrene (PS) and poly(methyl methacrylate) (PMMA) was modified by an intermediate layer of either a premade poly(styrene-g-methyl methacrylate) copolymer (P(S-g-MMA)) or a preblend of mutually reactive PS and PMMA synthesized by atom transfer radical polymerization (ATRP). No significant difference was found in the interfacial fracture toughness measured by the double cantilever beam test, although the morphology of the interfacial region was not the same when observed by transmission electron microscopy. The premade copolymer formed a distinct interphase, in contrast to the sharp interface that was observed in the case of the reactive system. The analysis of the fracture surfaces by Raman confocal microscopy showed that the fracture occurred alternatively in the PS phase and either at the PS/copolymer interface for the non reactive system or at the PS/PMMA interface for the reactive one.