Structural development of natural rubber during uniaxial stretching by in situ wide angle X-ray diffraction using a synchrotron radiation

Structural development of natural rubber during uniaxial stretching was examined by an in situ wide angle X-ray diffraction measurement using a synchrotron. During stretching, the amorphous part showed little change, i.e. an amorphous halo remained clear even at 500% strain. The fraction of induced crystals was very small, though a clear crystalline pattern was observed at 400% strain. Some polymer chains were oriented and crystallized, but most of the chains were not oriented at all in spite of large deformations of the specimen. Only a small amount of polymer chains contributes to the stress and hysteresis loss during elongation.