Rheological and thermal properties of m-LLDPE blends with m-HDPE and LDPE

The dynamic and steady state behavior of metallocene linear low density polyethylene (m-LLDPE) blended with metallocene high density polyethylene (m-HDPE) and with low density polyethylene (LDPE) were measured in parallel plate rheometer at 160, 180, and 200 °C. The composition dependence of zero shear viscosity η0, the characteristic relaxation time τ0 and the characteristic frequency ω0 of m-LLDPE/m-HDPE blends show a linear variation in the whole range of weight fraction, which indicates that m-LLDPE/m-HDPE blends are miscible blend. At the same time, m-HDPE showing a ‘dissident’ rheological behavior should possess a certain very low degree of LCB. Two calculation methods of LCB verify this point. In contrast, the composition dependence of zero shear viscosity η0 of m-LLDPE/LDPE blends shows a positive deviation from the log-additivity rule, which can be well fitted by using the immiscible blend equation of Utracki. The characteristic relaxation time τ0 and the characteristic frequency ω0 have a sharp variation with the small amounts of LDPE in the blends, which also indicates a phase separation in the system. The thermal properties of m-LLDPE/m-HDPE blends are very similar to a single-component system. However, m-LLDPE/LDPE blends are immiscible in both melt and crystal states. DSC results are consistent with the rheological properties of these two series of blends.