Preparation of poly(vinyl phosphate-b-styrene) copolymers and its blend with PPO as proton exchange membrane for DMFC applications

Poly(vinyl phosphate-b-styrene) (poly(VPP-b-St)) block copolymers were prepared via consecutive telomerization of vinyl acetate (VAc), atom transfer radical polymerization (ATRP) with styrene, saponification, and phosphorylation with phosphorus oxychloride. The resulting block copolymers were characterized by FT-IR and pH titration. Then, the block copolymers were blended with poly(2,6-dimethyl-1,4-phenylene oxide) (PPO) to prepare direct methanol fuel cell (DMFC) membrane. The performance of poly(VPP-b-St)/PPO blend membranes was measured in terms of proton conductivity, methanol permeability, thermal and hydrolytic stability. The proton conductivities were in the range of 10− 4 to 10− 2 S/cm (60 °C, RH = 95%); the methanol permeabilities were in the range of 4.14 × 10− 8 to 9.62 × 10− 8 cm2/s (25 °C), and quite lower than that of Nafion® 117. Also, the thermal stability of the blend membranes was characterized by TGA, and was stable up to 400 °C; the blend membranes had better hydrolytic stability.