Effects of freeze-drying on the glass temperature of cyclic polystyrenes

The calorimetric glass temperature was measured for three cyclic polystyrenes with apparent molecular weights ranging from 4.0×103 to 195.5×103 g/mol for both bulk material and for samples freeze-dried from dilute solution. Freeze-drying from dilute solution was found to reduce the glass temperature by 7–14 K depending on the sample. These Tg depressions are 5–12 K greater than those found previously for freeze-dried linear polystyrene. Annealing at 403.2 and 443.2 K (130 and 170 °C) resulted in recovery of the Tg back to the bulk value with the time scales depending on both temperature and the magnitude of the Tg reduction; the low apparent activation energy dependence of the recovery of Tg precludes its being due to viscous flow.