Colorless polyimides from 2,3,3′,4′-biphenyltetracarboxylic dianhydride (α-BPDA) and various aromatic bis(ether amine)s bearing pendent trifluoromethyl groups

A series of organosoluble and light-colored polyimides (III) was prepared from 2,3,3′,4′-biphenyltetracarboxylic dianhydride (α-BPDA) with various fluorinated aromatic bis(ether amine)s via two-step method with thermal or chemical imidization of poly(amic acid)s yielded polyimides. The III series had inherent viscosity of 0.74–1.01 dl/g and showed excellent solubility in a variety of organic solvents. They were soluble in the amide polar solvent, ether-type solvent, and chlorinated solvent. These polyimide films also showed a high optical transparency and less color intensity, with an ultraviolet-visible absorption edge of 369–382 nm and low b* values (a yellowness index) of 5.0–11.7. Glass-transition temperature of the III series was recorded at 244–319 °C and higher than the isomeric polyimides V series. Compared with the nonfluorinated polyimides IV, the III series showed lighter-colored and lower dielectric constants and moisture absorptions. The good tensile properties and excellent thermal properties of the III series were also observed.