Fluorescence and IR characterization of epoxy cured with aliphatic amines

Cure reactions of the stoichiometric mixtures of diglycidyl ether of bisphenol A (DGEBA) and two very low molecular weight aliphatic polyether diamines (PED) were studied by using fluorescence and mid- and near-IR spectroscopic techniques. As the cure proceeded, the primary amine groups in PED are converted to the secondary and the tertiary amines. Near-IR spectral analysis was used to calculate the concentration of the three amine groups as a function of cure time. The decrease in the fluorescence intensity of DGEBA at about 307 nm was observed due to more effective quenching of the tertiary amine groups in PED, in comparison to the primary and the secondary amine groups. A large decrease in fluorescence intensity at 75 and 95 °C cure was observed. The amount of all the amine species was estimated from NIR spectra to shed light on the cure kinetics of PPO (polypropylene oxide) in comparison with PEO (polyethylene oxide) epoxy, as well as to explain their fluorescence behavior. uorescence intensity changes were correlated to the extent of epoxy reaction obtained by mid- and near-IR spectroscopy.