A new class of high Tg and organosoluble polynaphthalimides

A new class of soluble six-membered ring polynaphthalimides (PNIs) was synthesized from asymmetrical fluorinated naphthalene-substituted monomers. All the resulting PNIs were easily soluble in many organic solvents, such as N-methyl-2-pyrrolidinone (NMP), N,N-dimethylacetamide (DMAc), dimethyl sulfoxide (DMSO), and chloroform. They also showed good thermal stability with glass transition temperature of 340–386 °C, 10% weight loss temperature in excess of 529 °C. Polyimide 3c could be solution-cast into tough and flexible film. The film had a tensile strength, elongation at break, and Youngʹs modulus of about 117.6 MPa, 23.6%, and 1.77 GPa, respectively. The gas permeation property of the film of 3c was investigated with oxygen permeability coefficient ( P O 2 = 3.99 ) and permeability selectivity coefficient of oxygen to nitrogen ( P O 2 / P N 2 = 5.27 ) . Therefore, these materials are expected to be a good alternative to PIs based on five-membered rings with applications in gas separation membranes.