Tailored surface properties of semi-fluorinated block copolymers by electrospinning

Diblock copolymers based on polystyrene (PS) macroinitiators and four different fluorinated monomers (perfluorooctyl ethyl methacrylate (FMA), pentafluorostyrene (FS), perfluorooctyl-ethylene oxymethyl styrene (EMS), 2,3,5,6-tetrafluoro-4-(3,3,4,4,5,5,6,6,7,7,8,8,9,9,10,10,10-heptadecafluorodecaoxy)styrene (FSF)) were synthesized via atom transfer radical polymerization (ATRP). The lengths of the PS and fluorinated blocks were altered and the surface and self-assembling properties of the polymers were compared with respect to the fluorinated monomer used and the fluorine content. The surface properties, contact angles and surface tension, were enhanced by the existence of the CF3 groups at the end of the alkyl chains compared with poly(pentafluorostyrene). Hydrophobicity of the surfaces was further enhanced by electrospinning the polymer solutions, which yielded superhydrophobic surfaces with water contact angles >150° for polymers having CF3 groups.