Characterization of PA6/EPDM-g-MA/HDPE ternary blends: The role of core-shell structure

In this work, the relationship between properties and morphologies of PA6/EPDM-g-MA/HDPE ternary blends was studied. Two processing methods (one- and two-step methods) were applied to prepare the PA6/EPDM-g-MA/HDPE ternary blends. The dependence of the phase morphology on interfacial interaction and processing method was discussed here. It was found that core-shell morphology (core: HDPE, shell: EPDM-g-MA in PA6 matrix) appeared in PA6/EPDM-g-MA/HDPE ternary blends, and in comparison to the blend prepared by one-step method, the core-shell morphology with thicker EPDM-g-MA shell appeared in the blend prepared by two-step method. In this case, a super toughened PA6 ternary blends with the Izod impact strength of 72.51 kJ/m2 which is 4–5 times higher than PA6/EPDM-g-MA binary blend and 9–10 times higher than pure PA6 could be achieved. Moreover, the rheological results indicated that the storage modulus of ternary blends was heavily dependent on the phase morphology. The core-shell structure with thicker EPDM-g-MA shell would weaken the contribution of interfacial energy to the storage modulus of ternary blends.