Hydroxyapatite nanorods/poly(vinyl pyrolidone) composite nanofibers, arrays and three-dimensional fabrics: Electrospun preparation and transformation to hydroxyapatite nanostructures

Electrospinning has been recognized as an efficient technique for fabricating polymer nanofibrous biomaterials. However, the study of electrospun inorganic biomaterials with well-designed three-dimensional (3-D) structures is still limited and little reported. In this study hydroxyapatite (HAp) nanorods with an average diameter of ∼7 nm and length of ∼27 nm were synthesized through a simple precipitation method and used for the fabrication of inorganic/organic [poly(vinyl pyrolidone) (PVP)] composite nanofibers by electrospinning in ethanol solution. 3-D fabrics and aligned nanofiber arrays of the HAp nanorods/PVP composite were obtained as precursors. Thereafter, 3-D single phase HAp fabrics, tubular structures and aligned nanofiber arrays were obtained after thermal treatment of the corresponding composite precursors. Cytotoxicity experiments indicated that the HAp fabric scaffold had good biocompatibility. In vitro experiments showed that mesenchymal stem cells could attach to the HAp fabric scaffold after culture for 24 h.