Reduction of dislocation density and improvement of optical quality in ZnO layers by MgO-buffer annealing

Optical properties of ZnO thin films with/without MgO-buffer annealing were investigated by low and room temperature photoluminescence measurements. The ZnO films were grown on c-sapphire substrates by plasma-assisted molecular-beam epitaxy employing a thin MgO-buffer layer. Dislocation density of ZnO layer was reduced from 5.3 × 109 to 1.9 × 109 cm−2 by annealing MgO-buffer prior to the growth of ZnO. The intensity of free exciton emission from the sample with MgO-buffer annealing was almost twice of that from the sample without annealing, while the deep level emission from the sample with MgO-buffer annealing was about 1/3 of that without annealing. The MgO-buffer annealing improves optical quality of overgrown ZnO films.