Author/Authors :
Bashkin، نويسنده , , I.O. and Izotov، نويسنده , , A.N. and Moravsky، نويسنده , , A.P. and Negrii، نويسنده , , V.D. and Nikolaev، نويسنده , , R.K. and Ossipyan، نويسنده , , Yu.A. and Ponyatovsky، نويسنده , , E.G. and Steinman، نويسنده , , E.A.، نويسنده ,
Abstract :
Photoluminescence (PL) spectra were measured on the C60 polymeric phase prepared from a single crystal and from a microcrystalline powder treated at pressures to 15 kbar and temperatures to 600 K. It was found that the high-pressure treatment resulted in a shift of the spectral intensity distribution to lower energies compared to the well-known spectrum of pristine C60. A set of new lines was observed. The PL spectrum of the high-pressure phase exhibited a distinct structure contrary to that of photopolymerized C60. The PL intensity of the high-pressure phase showed a non-monotomic temperature dependence with a slight minimumum around 150 K.