Title of article :
Synthesis, structure and properties of RbMgBO3
Author/Authors :
Kurbatov، نويسنده , , R.V. and Solovyov، نويسنده , , L.A. and Bazarov، نويسنده , , B.G. and Subanakov، نويسنده , , A.K. and Bazarova، نويسنده , , J.G.، نويسنده ,
Issue Information :
روزنامه با شماره پیاپی سال 2013
Abstract :
A double borate RbMgBO3 was newly synthesized by solid state reactions and the crystal structure were determined from powder X-ray diffraction data. It crystallizes in cubic space group P213 (a=6.9493(1) Å, V=335.60(1) Å3, Z=4). RbMgBO3 was melted at 865.5 °C. The existence of only BO3 groups was confirmed by IR analysis. The RbMgBO3 conductivity was measured (10−6−10−5 S/cm).
Keywords :
A. Borates , D. Conductivity , E. Powder X-ray diffractometry , C. Crystal structure