Glow-discharge nitriding and post-oxidising treatments of AISI H11 steel

Post-oxidising treatments can be performed to improve the corrosion resistance of nitrided steel components. The glow-discharge process appears particularly attractive, since it allows to carry out both nitriding and post-oxidising treatments in a single technological operation, simply varying the treatment atmosphere and the working conditions. In the present paper the effects of using air as the treatment atmosphere of glow-discharge post-oxidising treatment have been evaluated. Nitriding treatments were performed at 773 K for 5 h, and post-oxidising treatments were carried out at 623 and 773 K for 1 h. The nitriding and nitriding+post-oxidising treatments produce modified surface layers consisting of an outer compound layer and an inner diffusion layer. When the post-oxidising treatments are performed, the compound layer consists of an oxide layer on the top of the nitride layer. With a 623 K post-oxidising treatment the oxide layer consists mainly of magnetite, Fe3O4, while when post-oxidising is carried out at 773 K it consists essentially of hematite, Fe2O3. In the inner nitride layer iron (γ′-Fe4N, ε-Fe2–3N) and chromium (CrN) nitrides are present. In all the treated samples high hardness values are obtained in the modified layers. The hardness profiles of the post-oxidised samples are only slightly affected by the 773 K post-oxidising treatment. The corrosion resistance of the treated samples was tested and the results show that the nitriding+623 K post-oxidising treatment is able to significantly improve the corrosion resistance of the untreated and treated AISI H11 samples.