Thermodynamic modeling of Fe–Ti–Bi system assisted with key experiments

Phase equilibria of Fe–Ti–Bi ternary system have been studied in this work. Firstly, by using alloy sampling, the isothermal section of Fe–Ti–Bi ternary system at 773 K was determined, where the existence of a ternary phase Bi2FeTi4 was confirmed. Meanwhile, formation enthalpies of the intermediate phases BiTi2, Bi9Ti8 and Bi2FeTi4, were obtained with first-principles calculations. Based on experimental data of phase equilibria and thermodynamic properties in literatures along with the calculated formation enthalpies in this work, thermodynamic modeling of Ti–Bi binary system and Fe–Ti–Bi ternary system were carried out with the CALPHAD approach. A set of self-consistent thermodynamic parameters to describe the Gibbs energy for various phases in Fe–Ti–Bi ternary system was finally obtained, with which solidification processes of two typical Fe–Ti–Bi alloys could be reasonably explained.