TiAlNb intermetallic compound coating prepared by high velocity oxy-fuel spraying

Ti28.35Al63.4Nb8.25 (at.%) intermetallic compound coatings were sprayed onto 316 L stainless steel substrates by HVOF processes using various parameters. By varying the grit blasting pressure between 0.11 and 0.55 MPa, the effects of substrate roughness on the adhesion of TiAlNb thermal sprayed coatings were investigated. The microstructure, porosity and microhardness of the coatings were characterized by SEM, XRD, Image Analysis and Vickers hardness analysis. The tensile adhesion test (TAT) specified by ASTM C 633-79 was used to measure the tensile bonding strength of the coating. The results show that the coatings with substrate roughness of 8.33 μm displayed the best combined strength. TiAlNb coatings had a lamellar microstructure with different spraying parameters. The porosity, bonding strength, microhardness of coatings were assessed in relation to the spraying processes. The thickness of bond coat on the bond strength of coatings was also discussed.