Cathodic arc plasma deposition of nano-multilayered ZrN/AlSiN thin films

Thin films of ZrN/AlSiN were deposited on SKD 11 tool steel substrate using Zr and AlSi cathodes in an Ar/N2 gas mixture in a cathodic arc plasma deposition system. The influence of the AlSi cathode arc current and the substrate bias voltage on the mechanical and structural properties of the films was investigated. X-ray diffraction, electron probe micro-analysis, high resolution transmission electron microscopy, nanoindentation and profilometry were used to characterize the films. The ZrN/AlSiN thin films had a multilayered structure by rotating the substrate in which nano-crystalline ZrN layers alternated with amorphous AlSiN layers. The hardness of the films increased as the AlSi cathode arc current was raised from 35 to 40 A, and then decreased with a further increase of the current. The hardness of the films increased with the increase of the bias voltage from − 50 to − 100 V. Further increase in the bias voltage decreased the hardness. The films exhibited a maximum hardness of 38 GPa. With the increase of bias voltage, the residual stress of the films correlated well with the hardness.