Mechanical and wear characterization of electroless nickel-boron coatings

Nanocrystalline electroless nickel-boron deposits were synthesized on mild steel (St-37 ASTM A36) substrates and submitted to heat treatment under non-reactive atmosphere to enhance their properties. Their mechanical and tribological properties were investigated by various methods including nanoindentation, Taber wear testing and scratch tests. Their structural properties were also studied. rdness of the deposits increased from 900 to 1250 hv25 due to optimal crystallization of the nanocrystalline coating while the Taber wear index was halved after heat treatment. ratch tests resistance of the coatings was good in both as-deposited and heat treated conditions. chanisms inducing the modification of the mechanical and tribological properties were discussed and they were linked to the structural state of the material.