Proton conductivity and fuel cell performance of organic–inorganic hybrid membrane based on poly(methyl methacrylate)/silica

Organic–inorganic hybrid membranes based on poly(methyl methacrylate) (PMMA)/silica have been synthesized using a sol-gel technique for use in polymer electrolyte fuel cells (PEFCs). The properties of these membranes were characterized using X-ray diffraction, Fourier transform infrared spectroscopy, scanning electron microscopy and thermogravimetric analysis. The results indicate that these membranes are formed through hydrogen bonds between the carbonyl group of PMMA and the uncondensed alcohol functional groups of the inorganic clusters. The proton conductivity of these membranes is on the order of 10−1 S cm−1, and the 60PMMA–30SiO2–10P2O5 membrane displays the highest proton conductivity of 3.85 × 10−1 S cm−1 at 90 °C and 50% RH. The performance of a fuel cell using these membranes was tested. A maximum power density of 370 mW cm−2 is obtained at 80 °C, and the current density at 0.4 V remains almost unchanged during the 100-h test time under the test conditions. This class of hybrid membranes is an extremely promising material for use in PEFCs.