Graphite oxide/functionalized graphene oxide and polybenzimidazole composite membranes for high temperature proton exchange membrane fuel cells

Graphite oxide/polybenzimidazole synthesized by 3, 3′-diaminobenzidine and 5-tert-butyl isophthalic acid (GO/BuIPBI) and isocyanate modified graphite oxide/BuIPBI (iGO/BuIPBI) composite membranes were prepared for high temperature polymer proton exchange membrane fuel cells (PEMFCs). All membranes were loaded with different content of phosphoric acid to provide proton conductivity. The GO/BuIPBI and iGO/BuIPBI membranes were characterized by SEM which showed that the filler GO or iGO were well dispersed in the polymer matrix and had a strong interaction with BuIPBI, which can improve the chemical stability of BuIPBI membrane and support a higher acid content. The proton conductivities of the GO/BuIPBI and iGO/BuIPBI with high acid loading were 0.016 and 0.027 S/cm, respectively, at 140 °C and without humidity.