Poly(3-hydroxybutyrate-co-3-hydroxyvalerate) co-polymer production from a local isolate, Brevibacillus invocatus MTCC 9039

Accumulation of poly(3-hydroxybutyrate-co-3-hydroxyvalerate) [P(3HB-co-3HV)] co-polymer by a local isolate, Brevibacillus invocatus MTCC 9039 under batch mode was investigated under glucose, acetate and propionate-supplemented conditions. Cells harvested at the stationary phase of growth depicted maximum accumulation of poly-3-hydroxybutyrate (PHB), i.e. 3% of dry cell weight (dcw) at pH 7.0 and temperature 30 °C at 48 h of incubation. PHB accumulation reached up to 52% (dcw) under 3% glucose with 1% acetate supplementation. P(3HB-co-3HV) co-polymer synthesis was observed under propionate-supplemented condition, which reached up to 45% under 3% glucose with 1% propionate supplementation. Optimization of process parameters by response surface methodology (RSM) resulted into co-polymer accumulation up to 65% (dcw) at 2.08% glucose, 1.62% acetate, 0.75% propionate and 2.15 g l−1 KH2PO4 concentrations. This co-polymer exhibited comparable material properties with the commercial [P(3HB-co-3HV)] co-polymers, whereas the elasticity was tremendously high and could be comparable with polypropylene. Thus, B. invocatus MTCC 9039 is emerging as an interesting organism and could be exploited further for P(3HB-co-3HV) co-polymer production.