In situ chemical reduction and functionalization of graphene oxide for electrically conductive phenol formaldehyde composites

We report an efficient one-step approach to reduce and functionalize graphene oxide (GO) during the in situ polymerization of phenol and formaldehyde. The hydrophilic and electrically insulating GO is converted to hydrophobic and electrically conductive graphene with phenol as the main reducing agent. Simultaneously, functionalization of GO is realized by the nucleophilic substitution reaction of the epoxide groups of GO with the hydroxyl groups of phenol in an alkali condition. Different from the insulating GO and phenol formaldehyde resin (PF) components, PF composites are electrically conductive due to the incidental reduction of GO during the in situ polymerization. The electrical conductivity of PF composite with 0.85 vol.% of GO is 0.20 S/m, nearly nine orders of magnitude higher than that of neat PF. Moreover, the efficient reduction and functionalization of GO endows the PF composites with high thermal stability and flexural properties. A striking increase in decomposition temperature is achieved with 2.3 vol.% of GO. The flexural strength and modulus of the PF composite with 1.7 vol.% GO are increased by 316.8% and 56.7%, respectively.