Synthesis and rheological properties of cation-exchanged Laponite suspensions

In this paper we report our new approach to synthesize cation-exchanged Laponite suspensions. General observations of the prepared samples indicated that an aqueous suspension of 1 wt.% Laponite retained its free flowing liquid phase characteristics even after aging for several weeks. When bivalent cationic metals (Cu, Co, Ni) were ablated into the suspension, the strong charge of the crystal face was reduced and, on standing, the suspension gelled becoming highly viscous. This sol–gel transition was induced by the formation of a space-filled structure due to both van der Waals and electrostatic bonds between the positively charged rims and negatively charged faces. Rheological properties of such prepared suspensions were measured using a Brookfield DV-II Pro Viscometer with a small sample adapter (SSA18/13RPY). The yield strengths of 2.2 N/m2, 3.2 N/m2, and 1.7 N/m2 were measured for Ni-, Co-, and Cu-modified Laponite suspensions, respectively. These yield strengths are sufficiently high for suspending weighting materials such as barite which requires the gel strength of about 0.5 N/m2.