Magnetic properties of Ni–Cu–Mn ferrite system

Three groups according to the substitution of Cu2+ and Mn3+ in the system Ni1−xCuxFe2−yMnyO4 ferrite with x = 0.2, 0.5, 0.8, and y varying from 0.0 to 1.0 in steps of 0.25 are prepared by solid state reactions. The phases of the Ni1−xCuxFe2−yMnyO4 ferrite have been confirmed by X-ray diffraction (XRD). The results demonstrate that all of the synthesized materials are spinel with cubic unit cell and the lattice constant increased with increases of the Cu and Mn ions for all samples. The hyperfine interaction was studied by the Mössbauer spectroscopy at room temperature for all samples. The spectra of all samples show two well-resolved Zeeman patterns corresponding to A- and B-sites. The hyperfine field decreases with increasing Cu and Mn ions concentration. The Curie temperature, TC, was calculated from the temperature dependence of magnetization curves. The hysteresis curve recorded at room temperature shows that the samples are ferrimagnetic materials. The cation distribution was estimated from the results of Mössbauer spectroscopy and magnetic measurements.