Chitosan modified poly(l-lactide) microspheres as cell microcarriers for cartilage tissue engineering

The surfaces of poly(l-lactide) (PLLA) microspheres were modified by chitosan via a method of hydrolysis and grafting-coating to improve their compatibility to chondrocytes. The PLLA microspheres with a diameter of 74–150 μm were fabricated by an oil/water emulsion solvent evaporation method, followed by hydrolysis in alkaline solution to produce a larger number of carboxyl groups. Using water-soluble carbodiimide as a coupling reagent, chitosan was covalently grafted onto the microspheres. Due to the physical entanglement and insolubility at neutral pH, unbonded chitosan molecules were stably remained to yield a large amount of coated chitosan. Biological performance of the control PLLA and the chitosan-coated PLLA microspheres were assessed by in vitro culture of rabbit auricular chondrocytes. After 24 h and 7 d culture, the chitosan-coated PLLA microspheres, especially the ones with larger chitosan amount, exhibited stronger ability to promote cell attachment and proliferation, and maintain the secretion function of the chondrocytes. Therefore, the chitosan-coated PLLA microspheres can be potentially used as the injectable cell microcarriers for chondrogenesis in cartilage tissue engineering.