Effects of adhesive temperature on the early and 6-month dentin bonding

Objectives m of this study was to test the effect of adhesive temperature on the bond strength to dentin (μTBS) and silver nitrate uptake (SNU) of an ethanol/water (Adper Single Bond 2 [SB]) and an acetone-based (Prime&Bond 2.1 [PB]) etch-and-rinse adhesive system. s ttles of each adhesive were kept in various temperatures (5 °C, 20 °C, 37 °C and 50 °C) for 1 h previously to its application in the occlusal demineralized dentin of 40 molars. Bonded sticks (0.8 mm2) were tested in tension (0.5 mm/min) immediately (IM) or after 6 months (6 M) of water storage. Two bonded sticks from each hemi-tooth were immersed in silver nitrate and analyzed by SEM. Data were analyzed by two-way repeated measures ANOVA and Tukeyʹs test (α = 0.05). s nificant difference in μTBS was detected for both adhesives at 5 °C and 20 °C. The highest bond strength for PB was observed in the 37 °C group while for SB it was in the 50 °C. Significant reductions of bond strengths were observed for PB at 37 °C and SB at 50 °C after 6 M of water storage. Silver nitrate deposition was seen in all hybrid layers, irrespective of the group. Lower silver nitrate deposition (water trees) in the adhesive layer was seen for PB and SB at higher temperatures. sions ating or refrigeration of the adhesives did not improve their resin–dentin bond resistance to water degradation over time.