In situ observation of cyclic fatigue crack propagation of SiC-fiber/SiC composite at room temperature

In situ observation of cyclic fatigue crack propagation of SiC-fiber reinforced SiC composite at room temperature has been carried out by laser microscopy. Both smooth (unnotched) and notched specimens are used for tension-tension cyclic fatigue tests. Cracks initiate at the comers of large pores during loading in smooth specimens. In notched specimens cracks are formed at the interfaces between fibers and matrix that are connected to the notch. The balance between the fiber bridging in the wake of propagating crack tip and the breakage of bridged fibers by the degradation of interfaces maintains a steady cyclic crack propagation. Crack propagation rate gradually decreases with time after the maximum load being applied.