Long aging time thermal degradation of the ac conductivity and complex permittivity of conducting polypyrrole

The modification of the ac conductivity and the complex permittivity of conducting polypyrrole was monitored throughout a two years thermal aging at 343 K. Reduction of the cross-over frequency is correlated with the degradation of dc-conductivity, while the ac conductivity region corresponding to the so-called ‘universal’ dielectric relaxation remains practically insensitive during the first year of ageing, which implies a collective co-operativity among multiple degradation processes that yield a practically time-independent effective disordered environment. A broad dielectric loss peak recorded in fresh specimens splits into two distinct relaxations for intermediate stages of the annealing process. The aging-time evolution of the dc component and the relaxations are qualitatively analysed and time constants are determined.