Structural and dielectric properties of ferroelectric Sr1−xBaxBi2(Nb0.5Ta0.5)2O9 and Sr0.5Ba0.5Bi2(Nb1−yTay)2O9 ceramics

Ferroelectric Sr1−xBaxBi2(Nb0.5Ta0.5)2O9 and Sr0.5Ba0.5Bi2(Nb1−yTay)2O9 were synthesized by solid state reaction route. X-ray diffraction studies confirm the formation of single phase layered perovskite solid solutions over a wide range of compositions (x=y=0.0, 0.25, 0.50, 0.75 and 1). The lattice parameters and the Curie temperature (Tc) have been found to have linear dependence on x and y. Transmission electron microscopy (TEM) suggest the lowering of orthorhombic distortion with increasing Ba2+ substitution. Variations in microstructural features as a function of x and y were monitored by scanning electron microscopy (SEM). The dielectric constant at room temperature increases with increase in both x and y. Interestingly Ba2+ substitution on Sr2+ site induces diffused phase transition and diffuseness increases with increasing Ba2+ concentration.