Structure and formation process of (K,Na)-clinoptilolite

In order to synthesize (K,Na)-clinoptilolite, a (K,Na)-aluminosilicate slurry with a seed crystal was stirred at 30 °C for 4 days and then hydrothermally treated under homogeneous mixing conditions at 120 °C for 14 days. The Si/Al:(Na+K)/Si:K/(Na+K):H2O/Al molar ratio of the starting materials was 6.0:0.42:0.5:52.5. The formation process of (K,Na)-clinoptilolite was investigated by a variety of techniques. When the materials were hydrothermally treated up to 6 days, amorphous (K,Na)-aluminosilicate was formed. After the hydrothermal treatment for 8 days, irregular particles due to the amorphous (K,Na)-aluminosilicate disappeared and plate-like particles of (K,Na)-clinoptilolite were formed, indicating that the amorphous aluminosilicate crystallized as clinoptilolite. In addition, (Na+K)/Al molar ratio in the materials varied from 1.2 to 1.0, accompanying the decrease of cation exchange capacity. During the crystallization, the wavenumber of external linkages of TO bonds shifted to higher values, implying that the SiOSi and SiOAl bonds were formed.