Development and cytotoxicity evaluation of SiAlONs ceramics

SiAlONs are ceramics with high potential as biomaterials due to their chemical stability, associated with suitable mechanical properties, such as high fracture toughness and fracture resistance. The objective of this work was to investigate the mechanical properties and the cytotoxicity of these ceramic materials. Three different compositions were prepared, using silicon nitride, aluminum nitride and a rare earth oxide mixture as starting powders, yielding Si3N4–SiAlON composites or pure SiAlON ceramics, after hot-pressing at 1750 °C, for 30 min. The sintered samples were characterized by X-ray diffraction analysis (XRD) and scanning electron microscopy (SEM). Furthermore, hardness and fracture toughness were determined using the Vickerʹs indentation method. The biological compatibility was evaluated by in vitro cytotoxicity tests. Ceramic with elevated hardness, ranging between 17 and 21 GPa, and high fracture toughness of 5 to 6 MPa m1/2 were obtained. Since a nontoxic behavior was observed in the cytotoxicity tests, it may be assumed that SiAlON-based ceramics are viable materials for clinical applications.